Ingredient |
Ni |
Mn |
Fe |
|
Content |
99.5 |
0.10 |
0.15 |
|
Skin material specification |
Thickness |
≥0.1mm |
||
Width |
According to customers demand |
|||
Silk material specification |
≥0.1mm |
|||
Tensile strength |
≥43kgf/mm2 |
|||
Elongation ratio (L=100) |
≥15 |
|||
Characteristic and use |
It is an alloy product with nickel as the essential component. It has the fine mechanical strength, corrosion resistance performance and characteristic of high strength under high temperature. It is applied in manufacturing electronic vacuum devices, electronic instrumentation parts and so on. |
Grade | Tensile strengh,min,Mpa | Yield Strength,0.2% offset,Mpa | Elongation,min% | |||
M | m | M | m | M | m | |
Nickel 200 | 379 | 448 | 103 | 267 | 40 | 15 |
Nickel 201 | 345 | 414 | 83 | 207 | 40 | 15 |
Monel400 | 483 | 586 | 193 | 375 | 35 | 15 |
|
Density |
Melting point |
Coefficient of expansion |
Modulus of rigidity |
Modulus of elasticity |
Electrical resistivity |
Ni200 |
8.9g/cm3 |
1446°C |
13.3 µm/m °C (20-100°C) |
81kN/mm2 |
204kN/mm2 |
9.6μW• cm |
Ni201 |
1446°C |
13.1µm/m °C(20-100°C) |
82kN/mm2 |
207kN/mm2 |
8.5μW• cm |
Grade |
Element Composition/% |
|||||||
Ni+Co |
Mn |
Cu |
Fe |
C |
Si |
Cr |
S |
|
Ni201 |
≥99.0 |
≤0.35 |
≤0.25 |
≤0.30 |
≤0.02 |
≤0.3 |
≤0.2 |
≤0.01 |
Ni200 |
≥99.0 |
/≤0.35 |
≤0.25 |
≤0.30 |
≤0.15 |
≤0.3 |
≤0.2 |
≤0.01 |
Ingredient |
Ni |
Mn |
Fe |
|
Content |
99.5 |
0.10 |
0.15 |
|
Skin material specification |
Thickness |
≥0.1mm |
||
Width |
According to customers demand |
|||
Silk material specification |
≥0.1mm |
|||
Tensile strength |
≥43kgf/mm2 |
|||
Elongation ratio (L=100) |
≥15 |
|||
Characteristic and use |
It is an alloy product with nickel as the essential component. It has the fine mechanical strength, corrosion resistance performance and characteristic of high strength under high temperature. It is applied in manufacturing electronic vacuum devices, electronic instrumentation parts and so on. |
Grade | Tensile strengh,min,Mpa | Yield Strength,0.2% offset,Mpa | Elongation,min% | |||
M | m | M | m | M | m | |
Nickel 200 | 379 | 448 | 103 | 267 | 40 | 15 |
Nickel 201 | 345 | 414 | 83 | 207 | 40 | 15 |
Monel400 | 483 | 586 | 193 | 375 | 35 | 15 |
Grupos de Producto : Níquel / Titanio